316L rustfrit stål - Korrosionsbestandigt

Kraftige svejseapplikationer

In general, stainless steel is susceptible to intergranular corrosion due to the precipitation of chromium carbides between the grains during welding. It can also occur when carbon diffuses into the body of stainless steel from oil, plastic tape, and other organic substances under heat. The process is known as carburization. However, due to low carbon content, 316L thrives under such environments by offering excellent resistance to intergranular corrosion. Therefore, fabricators choose 316L over 316 in heavy gauge (>6 mm) svejsede komponenter.

 

Her er en kortfattet sammenligningstabel af 316L rustfrit stål med andre almindelige rustfrit ståltyper:

Rustfrit stål type	Korrosionsbestandighed	Trækstyrke	Vigtigste kemiske komponenter	Typiske omkostninger	Typiske applikationer
316L	Meget høj	Høj	16-18 % Cr, 10-14 % Ni, 2-3 % Mo,<0.03% C	Moderat	Medicinsk udstyr, marine miljøer, kemisk behandling
304	Høj	Moderat	18-20 % Cr, 8-12 % Ni,<0.08% C	Sænke	Køkkenudstyr, arkitektonisk beklædning
410	Moderat	Høj	11,5-13,5 % Cr,<0.15% C	Sænke	Bestik, damp og gasturbine vinger
321	Høj	Høj	17-19% Cr, 9-12% Ni, 5x%C Ti	Højere	Luftfartskomponenter, udstødningssystemer